Bone graft substitute composition

ABSTRACT

A composition includes calcium sulfate hemihydrate, stearic acid, an accelerant, and a mixing solution. The composition can be injected, e.g., through a needle, and is capable of setting, e.g., in vivo, in a relatively short period of time to a relatively high hardness.

CLAIM OF PRIORITY

[0001] This application claims priority under 35 U.S.C. §119(e) to U.S. Patent Application Serial No. 60/368,924, filed on Mar. 29, 2002, the entire contents of which are hereby incorporated by reference.

TECHNICAL FIELD

[0002] The invention relates to bone graft substitute compositions.

BACKGROUND

[0003] Compositions containing calcium sulfate can be used as filler for voids or defects defined by bone. In some embodiments, the compositions can promote bone growth.

SUMMARY

[0004] The invention relates to bone graft substitute compositions.

[0005] In one aspect, the invention features a composition including calcium sulfate, such as calcium sulfate hemihydrate, a binder, an accelerant, and a mixing solution.

[0006] In another aspect, the invention features a method including providing a mixture having calcium sulfate, such as calcium sulfate hemihydrate, a binder, and an accelerant, and contacting the mixture with a mixing solution.

[0007] Embodiments of the invention may include one or more of the following features. The calcium sulfate includes calcium sulfate hemihydrate. The binder includes stearic acid, hydroxypropylmethylcellulose (HPMC), hydroxymethylcellulose (HPC), and/or hyaluronic acid. The accelerant includes calcium sulfate dihydrate, and/or an ionic salt such as potassium sulfate, or sodium sulfate. The mixing solution includes a saline solution.

[0008] Embodiments may have one or more of the following advantages. The composition is capable of setting or hardening in a relatively short time. In embodiments, the composition can harden to about 4 MPa in about 5-10 minutes. The composition is capable of setting or hardening in vivo. The composition can be injected through a needle, e.g., an 11-13 gauge needle up to about 10 cm long.

[0009] Other features and advantages of the invention will be apparent from the description of the preferred embodiments thereof and from the claims.

DETAILED DESCRIPTION

[0010] A bone graft substitute composition includes calcium sulfate, such as calcium sulfate hemihydrate (CaSO₄.½H₂O), a binder, such as stearic acid, a material that accelerates hardening of the composition (“an accelerant”), and a mixing solution. In some embodiments, the calcium sulfate, the binder, and the accelerant are provided as a mixture of powders to which the mixing solution is added to form the composition. The composition can be delivered to a target site by injecting the composition through a needle. The composition can harden in vivo, e.g., such that the hardened composition is capable of supporting orthopedic hardware.

[0011] The calcium sulfate is preferably calcium sulfate hemihydrate, CaSO₄.½H₂O. Without wishing to be bound by theory, it is believed that during use, e.g., after mixing the powder mixture with the mixing solution, the calcium sulfate hemihydrate is converted, e.g., changes crystalline form, into calcium sulfate dihydrate (CaSO₄.½H₂O), which hardens the composition. Calcium sulfate dihydrate is capable of being sorbed by the body. In some embodiments, the mixture of powders includes greater than about 90 weight percent of calcium sulfate, e.g., calcium sulfate hemihydrate. The mixture may include greater than 90, 91, 92, 93, 94, 95, 96, 97, 98, or 99 weight percent of calcium sulfate hemihydrate; and/or less than 100, 99, 98, 97, 96, 95, 94, 93, 92, or 91 weight percent of calcium sulfate hemihydrate. Methods of making a calcium sulfate hemihydrate is described in U.S. Pat. Nos. 5,614,206, 5,807,567, and 6,030,636, all hereby incorporated by reference in its entirety.

[0012] Without wishing to be bound by theory, it is believed that the binder provides the composition with a consistency that helps the composition to flow, e.g., to be injectable. It is believed that, for example, stearic acid may also make the composition relatively hydrophobic, for example, which may lubricate the inner wall of a syringe and enhance flow of the composition. In some embodiments, the mixture of powders includes between about 1 and 2, e.g., about 1.5-2.0, weight percent of the binder. The mixture may include greater than 1.0, 1.1, 1.2, 1.3, 1.4, 1.5, 1.6, 1.7, 1.8, or 1.9 weight percent of the binder; and/or less than 2.0, 1.9, 1.8, 1.7, 1.6, 1.5, 1.4, 1.3, 1.2, or 1.1 weight percent of the binder. Examples of binders include stearic acid, hydroxypropylmethylcellulose (HPMC), hydroxymethylcellulose (HPC), and hyaluronic acid. Mixtures of two or more binders may be used.

[0013] Without wishing to be bound by theory, the accelerant is believed to enhance, e.g., accelerate, the conversion of calcium sulfate hemihydrate to calcium sulfate dihydrate. In particular, it is believed that particles of the accelerant act as crystallization nucleation sites for the conversion of calcium sulfate hemihydrate to calcium sulfate dihydrate. Examples of accelerants include calcium sulfate dihydrate, potassium sulfate, or sodium sulfate. Other examples include ionic salts. A preferred accelerant is calcium sulfate dihydrate crystals (available from U.S. Gypsum) coated with sucrose (available from VWR Scientific Products). A process of stabilizing the dihydrate crystals by coating with sucrose is described in U.S. Pat. No. 3,573,947, hereby incorporated by reference in its entirety. In some embodiments, the mixture of powders includes between about 0.1 and 0.5 weight percent of the accelerant. The mixture may include greater than 0.10, 0.15, 0.20, 0.25, 0.30, 0.35, 0.40, or 0.45 weight percent of the accelerant; and/or less than 0.50, 0.45, 0.40, 0.35, 0.30, 0.25, 0.20, or 0.15 weight percent of the accelerant. Mixtures of two or more accelerants can be used.

[0014] The mixing solution is generally selected to provide the composition with a desired consistency and hardening time. Examples of a mixing solution include water, e.g., sterile water, solutions containing inorganic salts, or cationic surface-active agents including sodium chloride, saline, e.g., phosphate buffered saline, potassium chloride, sodium sulfate, potassium sulfate, EDTA, ammonium sulfate, ammonium acetate, and sodium acetate. A specific example of a mixing solution is 0.9% NaCl saline solution (available from Baxter). In some embodiments, for a 25 g mixture of powders, preferably about 8-10 cc of mixing solution is added to the mixture to form a composition. Mixtures of two or more mixing solutions can be used.

[0015] The mixing solution can further include, for example, bone marrow aspirate, platelet concentrate, blood, pharmaceutical additives in solution, or combinations of these materials. Examples of additives are medicaments or pesticides. Examples of medicaments are antibiotics, chemotherapeutic agents, growth factors, and analgesics. Examples of antibiotics are tetracycline hydrochloride, vancomycin, cephalosporins, and aminoglycocides such as tobramycin and gentamicin. Examples of chemotherapeutic agents are cis-platinum, ifosfamide, methotrexate, and doxorubicin hydrochloride (Adriamycin®). Examples of growth factors are transforming growth factor beta (TGF-Beta), bone morphogenic protein (BMP), basic fiberblast growth factor, platelet-derived growth factor, and other polypeptide growth factors. Examples of analgesics are anesthetics such as lidocaine hydrochloride (Xylocaine®), bipivacaine hydrochloride (Marcaine®), and non-steroidal anti-inflammatory drugs such as ketorolac tromethamine (Toradol®). Certain mixing solution can affect, e.g., delay, the hardening properties of the composition.

[0016] The composition can be formed by providing the mixture of powders (e.g., calcium sulfate hemihydrate, stearic acid, and calcium sulfate dihydrate) and contacting, e.g., mixing, the mixture with a mixing solution (e.g., NaCl saline) to form the composition. The composition may be a conforming material having a paste-like consistency, e.g., like Plaster of Paris. The material can be injected into a target site, for example, to fill into cracks or voids. In some embodiments, the material can be injected through an 11 to 13-gauge needle up to, for example, 10 cm long. The material is capable of setting to a hardness comparable to or greater than bone within about 5-10 minutes, e.g., greater than 5, 6, 7, 8, or 9 minutes, and/or less than 10, 9, 8, 7, or 6 minutes. The material can have a Vicat set time of about 510 minutes, e.g., 5-6 minutes. The material is capable of hardening to about >4 MPa.

[0017] The hardened composition can be used for intra-operative support of hardware, such as orthopedic hardware, e.g., bone plates, distal radius hardware, and hardware used for tibial plateau fractures.

Other Embodiments

[0018] In some embodiments, the composition further includes a bioactive agent. Examples of bioactive agents include demineralized bone matrix, growth factors, hyaluronic acid, bone morphogenic proteins, bone autograft, and bone marrow, etc. The composition may include sodium bicarbonate. For example, the composition may include 0.1-2% sodium bicarbonate by weight to provide a porous structure in the resultant composition.

[0019] Alternatively or in addition, the bone graft substitute composition may include one or more additive such as an antiviral agent, an antimicrobial agent, an antibiotic agent, an amino acid, a peptide, a vitamin, an inorganic element, a protein synthesis co-factor, a hormone, an endocrine tissue, a synthesizer, an enzyme, a polymer cell scaffolding agent with parenchymal cells, an angiogenic drug, demineralized bone powder, a collagen lattice, an antigenic agent, a cytoskeletal agent, mesenchymal stem cells, a bone digester, an antitumor agent, an cellular attractant, fibronectin, a growth hormone, a cellular attachment agent, an immunosuppressant, a nucleic acid, a surface active agent, calcium phosphate materials, such as hydroxyapatite or tricalcium phosphate, a penetration enhancer, a bone allograft, cancellous bone chip (an osteoconductive substrate), and chunks, shards, and/or pellets of calcium sulfate.

[0020] The bone graft substitute composition can also be used as a carrier, for example, by mixing it with other materials, such as, for example, allografts, antibiotics, growth factors, cancellous bone chips, or synthetically derived or naturally derived chips of minerals such as calcium phosphate or calcium carbonate. This can provide the composition with versatility and flexibility by allowing a user to formulate a mixed composition according to a desired application.

[0021] The following example is illustrative and not intended to be limiting.

EXAMPLE

[0022] A 25-gram mixture of powders was formed having 98.08 wt % of CaSO₄.½H₂O, 1.77 wt % of stearic acid (triple pressed powder, available from VWR Scientific Products), and 0.15 wt % of CaSO₄.2H₂O. About 9 cc of mixing solution (0.9% NaCl saline) was added to the mixture of powders, and mixed together to form a composition having a paste-like consistency.

[0023] The composition could be injected through a 6 cm long, 11-gauge needle. After about 7 minutes, the composition hardened, e.g., comparable to the hardness of bone. More specifically, the composition hardened to about 8 MPa (8.17 MPa±0.23, n=3) after about twenty minutes; to about 17 MPa (16.54 MPa±1.05, n=8) after about one hour; and to about 35 MPa (34.94 MPa±4.04, n=5) after about 24 hours.

[0024] As described above, the composition can also harden in vivo. Following procedures similar to ASTM-F451, cylindrical samples (6 mm diameter, 12 mm high) of the composition were submerged in bovine calf serum to simulate in vivo conditions. The hardness of the samples was measured at different times. After about seven minutes, the composition hardened to about 1 MPa (1.04 MPa±0.29, n=3). After about twenty minutes, the composition hardened to about four MPa (3.82 MPa±0.87, n=3). After about one hour, the composition hardened to about 15 MPa (14.94 MPa±0.82, n=8). After about 24 hours, the composition hardened to about 10 MPa (10.59±0.73, n=8).

[0025] The amount of mixing solution added to the mixture of powders can affect the time the composition takes to set, i.e., the set time. Increasing the amount of mixing solution can increase the set time. For example, in embodiments, adding more than 12 cc of saline to the above 25-gram mixture may delay hardening to over 30-40 minutes. Decreasing the amount of mixing solution added to the mixture of powders can reduce the set time but injecting the composition can be relatively difficult.

[0026] Other embodiments are within the claims. 

What is claimed is:
 1. A kit, comprising: a mixture comprising calcium sulfate hemihydrate, calcium sulfate dihydrate, and a binder; and an aqueous mixing solution.
 2. The kit of claim 1, wherein the binder comprises stearic acid.
 3. The kit of claim 1, wherein the binder comprises a material selected from the group consisting of hydroxypropylmethylcellulose, hydroxymethylcellulose, and hyaluronic acid.
 4. The kit of claim 1, wherein the mixture comprises >95 wt % of calcium sulfate hemihydrate; about 0.1 to about 0.5 wt % of calcium sulfate dihydrate; and about 1.5 to about 2 wt % of the binder.
 5. The kit of claim 1, wherein the saline solution comprises sodium chloride.
 6. The kit of claim 1, wherein the calcium sulfate dihydrate comprises sucrose.
 7. A kit, comprising: a mixture comprising calcium sulfate hemihydrate, a first material selected from the group consisting of potassium sulfate and sodium sulfate, and a binder; and an aqueous mixing solution.
 8. The kit of claim 7, wherein the binder comprises stearic acid.
 9. The kit of claim 7, wherein the binder comprises a material selected from the group consisting of hydroxypropylmethylcellulose, hydroxymethylcellulose, and hyaluronic acid.
 10. The kit of claim 7, wherein the mixture comprises >95 wt % of calcium sulfate hemihydrate; about 0.1 to about 0.5 wt % of the first material; and about 1.5 to about 2 wt % of the binder.
 11. The kit of claim 7, wherein the saline solution comprises sodium chloride.
 12. A composition, comprising: calcium sulfate hemihydrate; calcium sulfate dihydrate; stearic acid; and a mixing solution, wherein the composition is capable of hardening to about 4 MPa within about 10 minutes.
 13. The composition of claim 12, wherein the composition is injectable.
 14. The composition of claim 13, wherein the composition is injectable through a 6 cm long, 11-gauge needle.
 15. The composition of claim 12, comprising: >95 wt % of calcium sulfate hemihydrate; about 0.1 to about 0.5 wt % of calcium sulfate dihydrate; and about 1.5 to about 2 wt % of stearic acid.
 16. A composition, consisting essentially of: calcium sulfate hemihydrate; calcium sulfate dihydrate; a binder; and a mixing solution.
 17. The composition of claim 16, wherein the binder includes stearic acid.
 18. The composition of claim 17, consisting essentially of: >95 wt % of calcium sulfate hemihydrate; about 0.1 to about 0.5 wt % of calcium sulfate dihydrate; and about 1.5 to about 2 wt % of stearic acid.
 19. A method, comprising: providing a mixture comprising: >95 wt % of calcium sulfate hemihydrate; about 0.1 to about 0.5 wt % of calcium sulfate dihydrate; and about 1.5 to about 2 wt % of stearic acid; and contacting the mixture with a saline solution to form a composition.
 20. The method of claim 19, further comprising injecting the composition through a needle. 